Chemical Mineral
Description
?
?
1.brief
?
? This is patent products for degreasing electron level and solar grade silicon slice in IT and solar battery area, and the patent number is ZL200710020269.6.? The product contain double group with good performance in emulsion saponifiation edulcoration to tallowvegetable oilmineral oilsoliquiodgrinding past , also in stripingcomplexing edulcoration to metal ion.
?
2.feature
?
1) double group in concentrate, specially be suitable for degreasing polluted silicon slice
2)be free from calcium, magnesium, metal, copper, lead and phosphor, and meet the requirement of ROHS.
3)low foam, no foam overflow in ultrasonic cleaning.
4)good degreasing performance to meet the requirement of high-accuracy IT area.
?
3. technical parameter
?
- - - -
????? classification project | JH-1015-1 | Test Standard???????????? |
Appearance | Colorless to yellowish liquid | visualization |
Specific weight | 1.150-1.250 | densimeter |
pH | ≥14 | PH instrument |
free alkalinity(piont) | 300-400 | CYFC |
- - - -
?
4. instructions
?
1) put pure water into cleaning tank till three-quarter, then, add A agent in 2% concentration, stir, then add B agent in 1% concentration, after that, add water till working level, last, heat the bath solution till working temperature.
2)need to change bath solution completely after degreasing certain amount silicon slice.
3) reduce exposed time in air to avoid oxidation.
4)working temperature 50-65 degree, disposal time: 2-5minutes.
?
5. notes.
?
1)solar bar can not touch water, need to dip into soliquiod or degreasing agent if can not clean in time
2)need to disposal solar bar in time as soon as it came into degreasing process to avoid air-dry.
3) keep solar bar wet when deguming to avoid air-dry.
4)to avoid fragment, need to shut down bubble switch of no1 and no2 tank when ultrasonic degreasing, then, turn on the switch after fixing.
5)need to change no5.6 and 7 tank after one cycle degreasing.
6)silicon slice can not be touched. The workers must work with gloves to avoid fingerprint.
7)to achieve the clearance,? need to spray silicon slice at least 30miniuts before degumming.
?
6. additions.
?
1)packing:20kg/carton(2kg/bottle),25kg/plastic barrel, 1000kg/barrel
2)validity time: one year
?
?
?
Read More
Changzhou Junhe Technology Stock Co.,Ltd
Zinc Flake Coating,Water Based Top Coat,Dip Spin Coating Machine
Address: 20FL., Zhongchuang Budg., Times Commerce Plaza, 396 Tongjiamg Ave, Changzhou, Jiangsu, P. R. of China,
Changzhou, Jiangsu
China, 213000
Tel: 86-519-85922787
Fax: 86-0519-85913023